低合金钢的牌号和化学成分
| 牌号 | 化学成分a, b, c（质量分数）/% |
| C | Si | Mn | P | S | Nb | V | Ti | Cr | Ni | Cu | Nd | Mo | B | Alse |
| 不大于 | 不小于 |
| Q345XZ | B/C | 0 .18 | 0 .50 | 1 .70 | 0 .020 | 0 .010 | 0 .07 | 0 .20 | 0 .20 | 0 .30 | 0 .50 | 0 .20 | 0 .012 | 0 .10 | — | — |
| D/E | 0 .015 |
| Q390XZ | B/C | 0 .18 | 0 .50 | 1 .70 | 0 .020 | 0 .010 | 0 .07 | 0 .20 | 0 .20 | 0 .30 | 0 .50 | 0 .20 | 0 .015 | 0 .10 | — | — |
| D/E | 0 .015 |
| Q420XZ | B/C | 0 .18 | 0 .50 | 1 .70 | 0 .020 | 0 .010 | 0 .07 | 0 .20 | 0 .20 | 0 .30 | 0 .50 | 0 .20 | 0 .015 | 0 .20 | — | — |
| D/E | 0 .015 |
| Q460XZ | C/D/E | 0 .18 | 0 .60 | 1 .80 | 0 .020 | 0 .010 | 0 .07 | 0 .20 | 0 .20 | 0 .30 | 0 .50 | 0 .20 | 0 .015 | 0 .20 | 0 .004 | 0 .015 |
| Q500XZ | C/D/E | 0 .18 | 0 .60 | 1 .80 | 0 .020 | 0 .010 | 0 .07 | 0 .20 | 0 .20 | 0 .60 | 0 .50 | 0 .20 | 0 .015 | 0 .20 | 0 .004 | 0 .015 |
| Q550XZ | C/D/E | 0 .18 | 0 .60 | 2 .00 | 0 .020 | 0 .010 | 0 .07 | 0 .20 | 0 .20 | 0 .60 | 0 .50 | 0 .20 | 0 .015 | 0 .20 | 0 .004 | 0 .015 |
| Q620XZ | C/D/E | 0 .18 | 0 .60 | 2 .00 | 0 .020 | 0 .010 | 0 .07 | 0 .20 | 0 .20 | 0 .60 | 0 .50 | 0 .20 | 0 .015 | 0 .20 | 0 .004 | 0 .015 |
| a 当需要加入细化晶粒元素时，钢中应至少含有 Al、Nb、V、Ti 中的一种。 加入的细化晶粒元素应在质量证明书中注明含量。b 当细化晶粒元素组合加入时，Nb+V+Ti≤0.22% , Mo+Cr≤0.30%。c Q460XZ及规定屈服强度较低牌号的碳当量 CEV≤0 . 45%,其余牌号 CEV≤0 . 48% 。碳当量的计算公式： CEV=C+Mn/ 6+ ( Cr+Mo+V)/5+ ( Ni+Cu)/15 。d 如供方能氮元素含量符合表中规定，可不进行氮含量分析。 如果钢中加入 Al、Nb、V、Ti等固氮合金元素，固氮含量应在质量证明书中注明。e 当测量全铝(Alt) 时，钢中 Alt≥0.020%。 |
合金钢的牌号和化学成分
| 牌号 | 化学成分（质量分数）a/% |
| C | Si | Mn | Cr | Mo |
| 30CrMo | 0 . 26~0 . 34 | 0 . 17~0 . 37 | 0 . 40~0 . 70 | 0 . 80~1 . 10 | 0 . 15~0 . 25 |
| 35CrMo | 0 . 32~0 . 40 | 0 . 17~0 . 37 | 0 . 40~0 . 70 | 0 . 80~1 . 10 | 0 . 15~0 . 25 |
| 42CrMo | 0 . 38~0 . 45 | 0 . 17~0 . 37 | 0 . 50~0 . 80 | 0 . 90~1 . 20 | 0 . 15~0 . 25 |
| a 钢中 P≤0.020% , S≤0.010% , Ni≤0.30% , Cu≤0.20%。 |
低合金钢钢管的力学性能
| 牌号 | 拉伸 | 冲击 |
| 抗拉强度 m MPaR | 下屈服强度 eL a MPaR | 断后伸长率 %A | 试验温度℃ | 冲击吸收能量 2犓VJ |
| 不小于 | 不小于 |
| Q345XZ | B | 470~630 | 345 | 23 | 20 | 50 |
| C | 0 |
| D | - 20 |
| E | - 40 | 40 |
| 牌号 | 拉伸 | 冲击 |
| 抗拉强度 m MPaR | 下屈服强度 eL a MPaR | 断后伸长率 %A | 试验温度℃ | 冲击吸收能量 2KVJ |
| 不小于 | 不小于 |
| Q390XZ | B | 490~650 | 390 | 22 | 20 | 50 |
| C | 0 |
| D | - 20 |
| E | - 40 | 40 |
| Q420XZ | B | 520~680 | 420 | 21 | 20 | 50 |
| C | 0 |
| D | - 20 |
| E | - 40 | 40 |
| Q460XZ | C | 550~720 | 460 | 20 | 0 | 50 |
| D | - 20 |
| E | - 40 | 40 |
| Q500XZ | C | 610~770 | 500 | 18 | 0 | 60 |
| D | - 20 | 50 |
| E | - 40 | 40 |
| Q550XZ | C | 670~830 | 550 | 16 | 0 | 60 |
| D | - 20 | 50 |
| E | - 40 | 40 |
| Q620XZ | C | 710~880 | 620 | 15 | 0 | 60 |
| D | - 20 | 50 |
| E | - 40 | 40 |
| a 如屈服不明显，可测定规定塑性延伸强度 p0.2 代替 eL 。RR |
合金钢钢管的纵向力学性能
| 牌号 | 拉伸 | 冲击 |
| 抗拉强度 m MPaR | 下屈服强度 eL a, b MPaR | 断后伸长率 %A | 断面收缩率 %Z | 冲击吸收能量 2KUJ |
| 壁厚 ≤16 mm | 壁厚＞16 mm |
| 不小于 | 不小于 |
| 30CrMo | 930 | 735 | 715 | 12 | 50 | 71 |
| 35CrMo | 980 | 835 | 815 | 12 | 45 | 63 |
| 42CrMo | 1 080 | 930 | 910 | 12 | 45 | 63 |
| a 如屈服不明显，可测定规定塑性延伸强度 p0.2 代替 eL 。RRb 当壁厚大于 30 mm 时，其拉伸性能由供需双方协商确定。 |